sandvik 15w welding flux - Sandvik Materials Technology
Transcrição
sandvik 15w welding flux - Sandvik Materials Technology
SANDVIK 15W WELDING FLUX DATASHEET Sandvik 15W is a basic welding flux for submerged arc welding giving good slag removal and a fine bead appearance. Its relatively high basicity makes it suitable for joining of the austenitic and duplex stainless steel when high impact strength is desired. Due to its low niobium content burn-off it can be used advantageously with stabilized wire electrodes. STANDARDS – ISO 14174: S A AF 2 CHEMICAL COMPOSITION (NOMINAL) % Chemical composition (nominal) % SiO₂ CaF₂ Al₂O₃ 7 50 40 APPLICATIONS FORMS OF SUPPLY Agglomerated non-alloying welding flux. WELD METAL CHARACTERISTICS Chemical composition (nominal) % The chemical compositions are typical all-weld metal results for the Sandvik wire listed. Element 19.12.3.L 20.25.5.LCu 22.8.3.L 25.10.4.L C 0.01 0.01 0.01 0.01 Si 0.5 0.5 0.7 0.5 Mn 1.5 1.4 1.2 0.3 Cr 18.1 19.6 22.6 24.5 Ni 12.3 25.0 8.6 9.5 Mo 2.6 4.5 3.1 4.0 Nb - - - - N - - 0.15 0.22 Mechanical properties 1 SANDVIK 15W Folha de dados atualizada 08/09/2016 13:54:22 (substitui todas as edições anteriores) Sandvik 15W is a high performance welding flux in many joining applications in the chemical, petrochemical and oil&gas industry. It is particularly suited for Sandvik's range of duplex wire electrodes (e.g. Sandvik 22.8.3.L/25.10.4.L) due to the highly neutral behaviour, which ensures an optimal balanced microstructure. Sandvik 15W gives the following mechanical properties for the filler wires below. Sandvik wire R p0.2 MPa R m MPa A% KV J 20°C -40°C -196°C 19.12.3.L 390 530 41 100 85 40 20.25.5.LCu 345 550 40 125 - 100 22.8.3.L 620 790 29 115 85 - 25.10.4.L FABRICATION Fabrication Welding data Direct current with electrode positive is normally used. Wire diameter, mm Current, A Voltage, V Travel speed, mm/min 1.2 250-450 28-32 200-400 2.4 300-500 29-34 250-500 3.2 400-600 30-35 250-600 4.0 500-700 30-35 250-600 Bulk weight 1.0 kg/l Basicity (Boniszewski) 1.9 Current capacity using 60 x 0.5 mm wire electrode 1200 A Flux consumption 0.5 kg/kg wire electrode at 28 V 0.6 kg/kg wire electrode at 31 V 0.8 kg/kg wire electrode at 34 V Disclaimer: Recommendations are for guidance only, and the suitability of a material for a specific application can be confirmed only when we know the actual service conditions. Continuous development may necessitate changes in technical data without notice. This datasheet is only valid for Sandvik materials. www.smt.sandvik.com/contact-us SMT.SANDVIK.COM Folha de dados atualizada 08/09/2016 13:54:22 (substitui todas as edições anteriores) FLUX DATA