Wood Free Riviera Sinar Royal White produzido por Tjiwi Kimia 70 e
Transcrição
Wood Free Riviera Sinar Royal White produzido por Tjiwi Kimia 70 e
i a m / 2 2 May 2010 C Edition PT. PABRIK KERTAS TJIWI KIMIA SPECIFICATION OF WOOD FREE SINAR ROYAL WHITE Physical Test Test Method Kind of Test Reference Grammage, g/m² T410 om-98 Thickness, μm T411 om-97 *Basic-Weight*(g/m²) 70 74 75 80 89 90 100 105 110 70 ± 4% 74 ± 4% 75 ± 4% 80 ± 4% 89 ± 4% 90 ± 4% 100 ± 4% 105 ± 4% 110 ± 4% 90 ± 4 95 ± 4 96 ± 4 102 ± 4 111 ± 4 112 ± 4 125 ± 5 135 ± 5 142 ± 5 Roughness, ml/min ISO 8791/2/90 Brightness, %ISO (C/2°) ISO 2470-1999 93 ± 1 93 ± 1 93 ± 1 93 ± 1 93 ± 1 93 ± 1 93 ± 1 93 ± 1 93 ± 1 Opacity, % ISO 2471-1999 > 89 > 90 > 90 > 91 > 92 > 92 > 94 > 94.5 > 95 > 0.22 > 0.25 > 0.26 > 0.32 > 0.39 > 0.40 > 0.58 > 0.60 > 0.80 > 0.11 > 0.12 > 0.12 > 0.16 > 0.21 > 0.22 > 0.30 > 0.32 > 0.40 > 5.0 > 5.3 > 5.4 > 5.5 > 5.6 > 5.7 > 6.0 > 6.2 > 6.5 > 2.5 > 2.6 > 2.7 > 2.8 > 2.9 > 3.0 > 3.2 > 3.4 > 3.6 > 14 > 14 > 14 > 14 > 14 > 14 > 14 > 14 > 14 Stiffness, mN.m Tensile, kg/15mm MD CD MD CD T535 om-96 T494 om-96 Wax Pick, °A T459 om-93 Moisture, % T412 om-94 18/out/08 200 ± 50 200 ± 50 200 ± 50 200 ± 50 200 ± 50 200 ± 50 200 ± 50 200 ± 50 200 ± 50 6.0 ± 0.5 6.0 ± 0.5 6.0 ± 0.5 6.0 ± 0.5 6.0 ± 0.5 6.0 ± 0.5 6.0 ± 0.5 6.0 ± 0.5 6.0 ± 0.5 Acknowledged Quality Assurance GEORGE LEE CHRESNO JUNIARSO QA Manager 22/mai/10 # # # # # # # maio YYYY C Edition PT. PABRIK KERTAS TJIWI KIMIA SPECIFICATION OF WOOD FREE SINAR ROYAL WHITE Physical Test Test Method Kind of Test Reference Grammage, g/m² T410 om-98 Thickness, μm T411 om-97 *Basic-Weight*(g/m²) 115 120 130 135 140 150 160 170 115 ± 4% 120 ± 4% 130 ± 4% 135 ± 4% 140 ± 4% 150 ± 4% 160 ± 4% 170 ± 4% 145 ± 5 159 ± 5 163 ± 5 172 ± 5 178 ± 5 190 ± 5 205 ± 5 215 ± 6 Roughness, ml/min ISO 8791/2/90 Brightness, %ISO (C/2°) ISO 2470-1999 93 ± 1 93 ± 1 93 ± 1 93 ± 1 93 ± 1 93 ± 1 93 ± 1 93 ± 1 Opacity, % ISO 2471-1999 > 96 > 96.5 > 97 > 97.5 > 98 > 99 > 99 > 99 > 0.90 > 1.00 > 1.40 > 1.60 > 1.80 > 2.00 > 2.20 > 2.80 > 0.45 > 0.50 > 0.70 > 0.75 > 0.80 > 1.00 > 1.20 > 1.60 > 6.7 > 7.0 > 7.3 > 7.6 > 7.9 > 8.5 > 9.0 > 10.0 > 3.7 > 3.8 > 4.0 > 4.2 > 4.5 > 5.0 > 5.3 > 6.0 > 14 > 14 > 14 > 14 > 14 > 14 > 14 > 14 Stiffness, mN.m Tensile, kg/15mm MD CD MD CD T535 om-96 T494 om-96 Wax Pick, °A T459 om-93 Moisture, % T412 om-94 18/out/08 200 ± 50 200 ± 50 200 ± 50 200 ± 50 200 ± 50 200 ± 50 200 ± 50 200 ± 50 6.0 ± 0.5 6.0 ± 0.5 6.0 ± 0.5 6.0 ± 0.5 6.0 ± 0.5 6.0 ± 0.5 6.0 ± 0.5 6.0 ± 0.5 Acknowledged Quality Assurance GEORGE LEE CHRESNO JUNIARSO QA Manager 22/mai/10 # # # # # # # maio YYYY C Edition PT. PABRIK KERTAS TJIWI KIMIA SPECIFICATION OF WOOD FREE SINAR ROYAL WHITE Physical Test Test Method Kind of Test Reference Grammage, g/m² T410 om-98 Thickness, μm T411 om-97 *Basic-Weight*(g/m²) 175 180 190 200 210 230 250 270 175 ± 4% 180 ± 4% 190 ± 4% 200 ± 4% 210 ± 4% 230 ± 4% 250 ± 4% 270 ± 4% 221 ± 6 227 ± 6 239 ± 6 255 ± 6 273 ± 7 295 ± 7 310 ± 7 330 ± 7 Roughness, ml/min ISO 8791/2/90 Brightness, %ISO (C/2°) ISO 2470-1999 93 ± 1 93 ± 1 93 ± 1 93 ± 1 93 ± 1 93 ± 1 93 ± 1 93 ± 1 Opacity, % ISO 2471-1999 > 99 > 99 > 99 > 99 > 99 > 99 > 99 > 99 > 2.90 > 3.00 > 3.20 > 5.20 > 5.50 > 6.00 > 8.00 > 8.50 > 1.65 > 1.70 > 1.90 > 2.60 > 2.80 > 3.50 > 4.20 > 4.50 > 10.5 > 11.0 > 11.6 > 11.9 > 12.5 > 12.9 > 14.0 > 15.1 > 6.25 > 6.5 > 6.9 > 7.4 > 7.8 > 8.2 > 9.0 > 9.7 > 14 > 14 > 14 > 14 > 14 > 14 > 14 > 14 Stiffness, mN.m Tensile, kg/15mm MD CD MD CD T535 om-96 T494 om-96 Wax Pick, °A T459 om-93 Moisture, % T412 om-94 200 ± 50 200 ± 50 200 ± 50 200 ± 50 200 ± 50 200 ± 50 200 ± 50 200 ± 50 6.0 ± 0.5 6.0 ± 0.5 6.0 ± 0.5 6.0 ± 0.5 6.0 ± 0.5 6.0 ± 0.5 6.0 ± 0.5 6.0 ± 0.5 Acknowledged Quality Assurance GEORGE LEE CHRESNO JUNIARSO QA Manager 22/mai/10